1, the modulation glue is directly related to the glass fiber and magnesium duct in the prevention of cracking on the importance of representation; glue is too thick or too thin will make the wind pipe interface cracking, so in the modulation of the time bound to grasp consistency.

2、鹵水的濃渡過高或過低所致使的風(fēng)管開裂表象；通常復(fù)合風(fēng)管的制造人員都會(huì)把鹵水濃度定在一個(gè)標(biāo)準(zhǔn)上或是憑覺得來調(diào)制鹵水的濃度.

2, the brine concentration is too high or too low caused by the wind pipe cracking appearance; usually composite wind pipe manufacturers will put the brine concentration on a standard or on the basis of the concentration of brine

3、夏天在調(diào)制鹵水的時(shí)分由于氣溫很高所以要把濃度控制在21-23度左右，在初調(diào)的時(shí)分只需能抵達(dá)21 度就能夠了，由于鹵片消融的時(shí)間比照長(zhǎng)，等鹵片完整消融后再去檢驗(yàn)濃度這樣比照準(zhǔn)確。

In the summer of 3, when the modulation brine temperature is high so the concentration control in 21-23 degrees, in the early hours of just to reach 21 degrees can, because the bittern ablation time by long, such as halogen tablets after ablation to complete this concentration by accurate inspection.

4、冬天的氣溫較低，所以在調(diào)制鹵水時(shí)應(yīng)該把濃度控制在25-28度左右，同樣在初調(diào)的時(shí)分濃度應(yīng)該控制在25度左右等完整化開后再去丈量濃度。

4, the winter temperature is low, so in the modulation of brine should be controlled in the concentration of about 25-28 degrees, the same time at the beginning of the concentration should be controlled at around 25 degrees after the completion of the integrity of the measured concentration.

5、組合風(fēng)管時(shí)應(yīng)該把膠水調(diào)制的稀點(diǎn)，調(diào)好后手抓時(shí)膠水能自動(dòng)流出。銜接時(shí)的膠水應(yīng)該調(diào)制到和泥灰稠度成比照不能過于太稀。

5, combined wind pipe should put some glue diluted modulation, good hand grasping glue can automatically flow. The glue should be glued to the consistency of the paste and not too thin.

本文由山東通風(fēng)管道加工廠家為您提供，我們的網(wǎng)站是:http://888qp03.com/ 我們將以全心全意的熱情為您提供更的服務(wù)，歡迎您的訪問！

This article by the Shandong ventilation pipe processing factory to provide you, our website is: http://888qp03.com/ we will be dedicated to provide you with the best quality service, welcome your visit!